Lote & Laser-Schweissdrähte
Materialien für die verschiedenen Fügetechniken wie Löten oder Laserschweißen – für das sichere Verarbeiten von Ivoclar Vivadent Legierungen.
Laserschweißdrähte
Bezeichnung Farbe | Schmelzintervall |
Zusammensetzung in % |
Portadur IN gelb │ 940-1020 °C | Au 87,9 | Pt 4,0 | Ag 5,0 | Zn 3,0 | Ir < 1,0 |
Laser Ceramic Yellow PdF gelb | 1055-1170 °C | Au 85,9 | Pt 12,09 | In < 1,0 | Zn 1,5 | Fe < 1,0 | Mn < 1,0 | Ir < 1,0 | Ta < 1,0 |
BioPorta G gelb | 1040-1110 °C | Au 85,5 | Pt 11,5 | In < 1,0 | Zn 1,5 | Fe < 1,0 | Rh < 1,0 | W < 1,0 |
Laser Ceramic Yellow gelb | 1085-1215 °C | Au 85,0 | Pt 7,5 | Pd 3,0 | Ag 3,0 | In 1,5 | Ir < 1,0 |
Porta P6 weiß | 1110-1200 °C | Au 78,0 | Pt 9,8 | Pd 8,0 | In 4,0 | Ir < 1,0 | Sn < 1,0 |
Porta Geo Ti gelb | 1060-1140 °C | Au 77,4 | Pt 18,0 | Ag 2,0 | Zn 1,8 | Ti < 1,0 | Rh < 1,0 |
Laser C&B Yellow gelb | 900-960 °C | Au 75,0 | Pt 3,0 | Ag 13,5 | Cu 7,0 | In 1,5 | Ir < 1,0 |
Porta Norm gelb | 910-990 °C | Au 73,8 | Pt 9,0 | Ag 9,2 | Cu 4,4 | In 1,5 | Zn 2,0 | Ir < 1,0 |
Portadur P2 gelb | 890-930 °C | Au 71,0 | Pt 2,5 | Pd 1,5 | Ag 12,2 | Cu 12,2 | Zn < 1,0 | Ir < 1,0 |
Portadur P4 gelb | 920-970 °C | Au 68,5 | Pt 6,9 | Ag 12,0 | Cu 12,0 | Zn < 1,0 | Ir < 1,0 |
Laser Ceramic White weiß | 1200-1290 °C |
Au 50,0 | Pd 24,4 | Ag 21,5 | In 4,0 | Ru < 1,0 |
Laser C&B White weiß | 985-1025 °C |
Au 18,5 | Pd 6,0 | Ag 72,5 | In 3,0 | Ir < 1,0 |
Porta Smart weiß | 1370-1390 °C |
Co 65,1 | Cr 28,0 | Mo 5,9 | Mn < 1,0 | Si < 1,0 |
Vorlote
Bezeichnung Farbe | Schmelzintervall | Fließpunkt |
Zusammensetzung in % |
Porta Optimum Lot 940 gelb | 850-930 °C | 940 °C |
Au 89,0 | Pt 5,0 | Zn 5,7 | Ir < 1,0 |
Porta IP Lot V-1 gelb | 1015-1055 °C | 1070 °C |
Au 80,0 | Pt 1,9 | Ag 17,5 | In < 1,0 | Sn < 1,0 |
Porta Optimum Lot 880 gelb | 860-880 °C | 880 °C |
Au 75,5 | Ag 12,4 | Cu 9,5 | Zn 2,5 | Ir < 1,0 |
Bio Porta Lot 1020 gelb | 960-1010 °C | 1020 °C |
Au 73,5 | Ag 25,0 | Zn 1,5 |
Porta IP Lot V-2 gelb | 1015-1030 °C | 1040 °C |
Au 64,0 | Pt < 1,0 | Ag 34,9 | In < 1,0 | Ir < 1,0 |
HGPKF 1030 Y gelb | 1015-1040 °C | 1030 °C | Au 63,2 | Ag 35,0 | Mn < 1,0 | Zn < 1,0 | Pt < 1,0 | Ir < 1,0 |
Auropal Lot M-1 gelb | 710-770 °C | 800 °C | Au 62,0 | Pd 3,0 | Ag 17,0 | Cu 7,0 | In 5,0 | Zn 6,0 |
HGPKF 1015 Y gelb | 975-1035 °C | 1015 °C | Au 60,0 | Ag 36,5 | In < 1,0 | Zn < 1,0 | Pt < 1,0 | Ir < 1,0 | Sn < 1,0 |
Porta Lot 1090 W weiß | 900-1090 °C | 1090 °C |
Au 49,7 | Pd 13,0 | Ag 32,5 | Zn 4,5 | Ir < 1,0 |
Special High Fusing White Ceramic Solder (SHFWC) weiß | 1045-1105 °C | 1105 °C | Au 47,0 | Pd 10,3 | Ag 41,0 | In 1,4 | Ru < 1,0 | B < 1,0 | Ca < 1,0 | Ti < 1,0 |
High Fusing White Ceramic Solder (HFWC) weiß | 1100-1165 °C | 1135 °C | Au 45,0 | Pd 12,4 | Ag 41,5 | In 1,0 | Li < 1,0 | Ru < 1,0 |
Universallote
Bezeichnung Farbe | Schmelzintervall | Fließpunkt |
Zusammensetzung in % |
Porta OP Lot M-1 gelb | 750-810 °C | 820 °C |
Au 71,5 | Pt 1,0 | Ag 17,5 | Zn 10,0 |
Universal Solder PKF gelb | 800-900 °C | 850 °C | Au 48,8 | Pt 2,8 | Ag 40,5 | Zn 7,3 | In < 1,0 | Ir < 1,0 |
Universal Solder 1015 W weiß | 985-1025 °C | 1015 °C |
Au 18,5 | Pd 6,0 | Ag 72,5 | In 3,0 | Ir < 1,0 |
Nachlote
Bezeichnung Farbe | Schmelzintervall | Fließpunkt |
Zusammensetzung in % |
Porta Optimum Lot 710 gelb | 680-700 °C | 710 °C |
Au 73,0 | Ag 12,4 | Zn 14,5 | Ir < 1,0 |
Porta OP Lot W-2 gelb | 710-765 °C | 770 °C |
Au 68,0 | Pt 1,0 | Ag 19,0 | Zn 12,0 |
.650 Fine Gold Solder gelb | 785-835 °C | 830 °C |
Au 65,0 | Ag 13,0 | Cu 19,6 | Ga 2,0 | Zn < 1,0 |
Auropal Lot W-2 gelb | 720-750 °C | 750 °C |
Au 62,0 | Ag 22,0 | Cu 4,0 | Zn 12,0 |
.615 Fine Gold Solder gelb | 690-775 °C | 775 °C |
Au 61,5 | Ag 13,1 | Cu 17,4 | In 7,6 | Zn < 1,0 |
.585 Fine Gold Solder gelb | 610-725 °C | 725 °C |
Au 58,5 | Ag 16,0 | Cu 18,0 | Ga 7,2 | Zn < 1,0 |
Low Fusing White Gold Solder (LFWG) weiß | 665-710 °C | 730 °C |
Au 56,1 | Ag 27,4 | In < 1,0 | Sn < 1,0 | Zn 15,8 |
Lot zum Löten von EM-Legierungen an CoCr-Legierungen
Bezeichnung Farbe | Schmelzintervall | Fließpunkt |
Zusammensetzung in % |
Stahlgoldlot Nr. 80 M-1 weiß | 860-920 °C | 920 °C |
Au 80,0 | Zn 5,0 | Ni 15,0 |
Stahlgoldlot Nr. 80 W-2 weiß | 800-860 °C | 870 °C |
Au 80,0 | Ag 1,0 | Zn 7,0 | Ni 10,0 | Co 2,0 |
Folie
Platinfolie .001
Dicke 0,025 mm